Synthesis and magnetic characterization of nickel ferrite nanoparticles prepared by co-precipitation route

Magnetic nanoparticles of nickel ferrite (NiFe₂O₄) have been synthesized by co-precipitation route using stable ferric and nickel salts with sodium hydroxide as the precipitating agent and oleic acid as the surfactant. X-ray diffraction (XRD) and transmission electron microscope (TEM) analyses confirmed the formation of single-phase nickel ferrite nanoparticles in the range 8-28 nm depending upon the annealing temperature of the samples during the synthesis. The size of the particles (d) was observed to be increasing linearly with annealing temperature of the sample while the coercivity with particle size goes through a maximum, peaking at ∼11 nm and then decreases for larger particles. Typical blocking effects were observed below ∼225 K for all the prepared samples. The superparamagnetic blocking temperature (T_B) was found to be increasing with increasing particle size that has been attributed to the increased effective anisotropy energy of the nanoparticles. The saturation moment of all the samples was found much below the bulk value of nickel ferrite that has been attributed to the disordered surface spins or dead/inert layer in these nanoparticles.