Synthesis and properties of thermoplastic polyimides with ether and ketone moieties |
| |
Authors: | Xiaohui Yu Xiaogang Zhao Changwei Liu Zewei Bai Daming Wang Guodong Dang Hongwei Zhou Chunhai Chen |
| |
Affiliation: | Alan G. MacDiarmid Institute, Jilin University, Changchun 130012, China |
| |
Abstract: | A series of polyimides containing ether and ketone moieties were synthesized from 1,3‐bis(4‐fluorobenzoyl) benzene and several commercially available dianhydrides via a conventional two‐step polymerization. The inherent viscosities of Polyamide acids ranged from 0.46 to 0.73 dL/g. Thermal properties, mechanical properties, and thermalplasticity of the obtained polimide films were investigated by focusing on the chemical structures of their repeat units. These films were amorphous, flexible, and transparent. All films displayed low Tgs (184–225 °C) but also excellent thermal stability, the 5% weight loss temperature was up to 542 °C under nitrogen. The films showed outstanding mechanical properties with the modulus up to 3.0 GPa and the elongation at break in the range of 8–160%. The uniaxial stretching of PI‐a at high temperature was studied owing to its excellent flexibility. The PI‐a had an elongation at break up to 1600% at 245 °C and the uniaxially stretched film exhibited a much higher modulus (3.9 GPa) and strength (240 MPa) than undrawn film. The results indicated that PI‐a can potentially be used to prepare materials such as fiber, ultra‐thin film or ultra‐high modulus film. All the obtained films also demonstrated excellent thermoplasticity (drop of E′ at Tg > 103) which made the polyimides more suitable for melt processing. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2878–2884, 2010 |
| |
Keywords: | polyimides synthesis thermoplastics thin films |
|
|