Radiation-induced polymerization of glass forming systems. VI. Polymerization rate at higher conversion in binary systems

The effect of temperature and composition on the inflection point in the time–conversion curve and the saturated conversion was investigated in the radiation-induced radical polymerization of binary systems consisting of a glass-forming monomer and a solvent. In the polymerization of completely homogeneous systems such as glycidyl methacrylate (GMA)–triacetin and hydroxyethyl methacrylate (HEMA)–propylene glycol systems, the time–conversion curve has an inflection point at polymerization temperatures between T_vm (T_v of monomer system) and T_vp (T_v of polymer system). Such conversions at the inflection point changed monotonically between 0 and 100% in this temperature range. T_v was found to be 30–50°C higher than T_g (glass transition temperature) and a monotonic function of composition (monomer–polymer–solvent). The acceleration effect continued to 100% conversion above T_vp, and no acceleration effect was observed below T_vm. The saturated conversion in homogeneous systems changed monotonically between 0 and 100% for polymerization temperatures between T_gm (T_g of monomer system) and T_gp (T_g of polymer system). T_g was also a monotonic function of composition. No saturation in conversion was observed above T_gp, and no polymerization occurred below T_gm. In the polymerization of completely heterogeneous systems such as HEMA–dioctyl phthalate, no acceleration effect was observed at any temperature and composition. The saturated conversion was 100% above T_g of pure HEMA, and no polymerization occurred below this temperature in this system.