| Abstract: | The effect of temperature on the four-center type photopolymerization has been investigated for p-phenylenediacrylic acid diethyl ester over a wide temperature range including crystal transition point (56°C) and melting point (96°C) of monomer. With the elevation of temperature between ?50 and 15°C, the polymerization rate in the initial stage increased and the degree of polymerization decreased monotonously, while the rate in the later stage decreased above ?25°C. With irradiation at above 25°C, the monomer crystals became sticky, and the polymerization was suppressed at the stage of oligomerization with low conversion. This tendency was enhanced above the crystal transition point, giving mainly dimer in low yield. Above the melting point, only radical polymerization occurred with the aid of oxygen. The steric configuration of the products in the crystalline state was 1,3-trans with respect to the cyclobutane ring. Peaks in NMR spectra of all products were assigned to the protons involved in four compounds up to tetramer. Various results obtained have been interpreted in terms of the change, as a function of temperature, from a topochemical polymerization which proceeds under a control of the monomer lattice to a photoinitiated vinyl-type polymerization in the disordered state. It is concluded that a rigid crystal lattice is indispensable for the four-center type photopolymerization to proceed smoothly. |