| 水溶性ZnO量子点制备及其光学性质 |
| |
| 引用本文： | 庄稼,迟燕华,刘猛.水溶性ZnO量子点制备及其光学性质[J].高等学校化学学报,2007,28(12):2246-2251. |
| |
| 作者姓名： | 庄稼 迟燕华 刘猛 |
| |
| 作者单位： | 1. 西南石油大学材料科学与工程学院,成都,610500
2. 西南科技大学化学系,绵阳,621002 |
| |
| 基金项目： | 国家自然科学基金
,
国家电分析化学重点实验室基金
,
四川省科技厅项目 |
| |
| 摘 要： | 利用3-巯丙基三乙氧基硅烷对ZnO进行表面修饰后沉积SiO2, 制备出水溶性SiO2包覆ZnO的量子点. 与直接采用正硅酸乙酯沉积包覆SiO2的ZnO量子点相比, 362 nm处的激子荧光发射峰的强度提高了将近4倍. 由于表面引入了巯基官能团, 量子点的水溶性明显提高, 稳定性增强, 即使在较高的盐浓度下也不会团聚. 通过改变条件, 制备出了发光波长在420 nm的蓝色荧光量子点.
|
| 关 键 词： | 氧化锌 水溶性量子点 表面包覆 光学性质 |
| 文章编号： | 0251-0790（2007）12-2246-06 |
| 收稿时间： | 2007-02-12 |
| 修稿时间： | 2007年2月12日 |
Preparation and Optic Properties of Water-Soluble ZnO Quantum Dots |
| |
| ZHUANG Jia,CHI Yan-Hua,LIU Meng.Preparation and Optic Properties of Water-Soluble ZnO Quantum Dots[J].Chemical Research In Chinese Universities,2007,28(12):2246-2251. |
| |
| Authors: | ZHUANG Jia CHI Yan-Hua LIU Meng |
| |
| Institution: | Department of Material Science and Engineering, Southwest Petroleum University, Chengdu 610500, China;;Department of Chemistry, Southwest University of Science and Technology, Mianyang 621002, China |
| |
| Abstract: | SiO2/ZnO water-soluble quantum dots were prepared by modification of(3-mercaptopropyl)tri-ethoxysilicane.The emission spectral peak of exciton fluorescence was raised by about 4 times in comparison with that of the quantum dots obtained by direct SiO2 deposit on ZnO without modification.The introduction of hydrosulfide group(HS-) on ZnO,renders the quantum dots good water solubility,unique fluorescent stability and anti-congregation even at higher NaCl concentration.The water soluble blue SiO2/ZnO quantum dots were also prepared by this method with some modification of the reaction conditions.The photogenic wavelength of this blue quantum dots was found to be 420 nm.The emission spectra were very symmetrical without obvious red tail.The full widths half maximum were only 46 nm. |
| |
| Keywords: | ZnO Water-soluble quantum dot Surface coating Optic property |