Growth and field emission of tungsten oxide nanotip arrays on ITO glass substrate |
| |
Authors: | Kai Huang |
| |
Affiliation: | School of Physics Science and Technology, Lanzhou University, Lanzhou 730000, China |
| |
Abstract: | High-density and uniformly aligned tungsten oxide nanotip arrays have been deposited by a conventional thermal evaporation on ITO glass substrates without any catalysts or additives. The temperature of substrate was 450-500 °C. It was shown that the tungsten oxide nanotips are single-crystal grown along [0 1 0] direction. For commercial applications, field emission of the tungsten oxide nanotip arrays was characterized in a poor vacuum at room temperature. The field emission behaviors are in agreement with Fowler-Nordheim theory. The turn-on field is 2.8 V μm−1 as d is 0.3 mm. The excellent field emission performances indicated that the tungsten oxide nanotip arrays grown by the present approach are a good candidate for application in vacuum microelectronic devices. |
| |
Keywords: | 81.07.&minus b 81.10.&minus h 79.70.+q |
本文献已被 ScienceDirect 等数据库收录! |