Synthesis, structure and physical properties of the new Zintl phases Eu11Zn6Sb12 and Eu11Cd6Sb12

Reported are the syntheses, crystal structure determinations from single-crystal X-ray diffraction, and magnetic properties of two new ternary compounds, Eu₁₁Cd₆Sb₁₂ and Eu₁₁Zn₆Sb₁₂. Both crystallize with the complex Sr₁₁Cd₆Sb₁₂ structure type—monoclinic, space group C2/m (no. 12), Z=2, with unit cell parameters a=31.979(4) Å, b=4.5981(5) Å, c=12.3499(14) Å, β=109.675(1)° for Eu₁₁Zn₆Sb₁₂, and a=32.507(2) Å, b=4.7294(3) Å, c=12.4158(8) Å, β=109.972(1)° for Eu₁₁Cd₆Sb₁₂. Their crystal structures are best described as made up of polyanionic and ribbons of corner-shared ZnSb₄ and CdSb₄ tetrahedra and Eu²⁺ cations. A notable characteristic of these structures is the presence of Sb-Sb interactions, which exist between two tetrahedra from adjacent layers, giving rise to unique channels. Detailed structure analyses shows that similar bonding arrangements are seen in much simpler structure types, such as Ca₃AlAs₃ and Ca₅Ga₂As₆ and the structure can be rationalized as their intergrowth. Temperature-dependent magnetization measurements indicate that Eu₁₁Cd₆Sb₁₂ orders anti-ferromagnetically below 7.5 K, while Eu₁₁Zn₆Sb₁₂ does not order down to 5 K. Resistivity measurements confirm that Eu₁₁Cd₆Sb₁₂ is poorly metallic, as expected for a Zintl phase.