Crystal structures and chemistry of double perovskites Ba2M(II)M′(VI)O6 (M=Ca, Sr, M′=Te, W, U)

Structures of the double perovskites Ba₂M(II)M ′(VI)O₆ (M=Ca, Sr, M′=Te, W, U) at room temperature have been investigated by the Rietveld method using X-ray and neutron powder diffraction data. For double perovskites with M=Sr, the observed space groups are I2/m (M′ =W) and (M′=Te), respectively. In the case of M=Ca, the space groups are either monoclinic P2₁/n (M′=U) or cubic (M′=W and Te). The tetragonal and orthorhombic symmetry reported earlier for Ba₂SrTeO₆ and Ba₂CaUO₆, respectively, were not observed. In addition, non-ambient X-ray diffraction data were collected and analyzed for Ba₂SrWO₆ and Ba₂CaWO₆ in the temperature range between 80 and 723 K. It was found that the rhombohedral structure exists in Ba₂SrWO₆ above room temperature between the monoclinic and the cubic structure, whereas the cubic Ba₂CaWO₆ undergoes a structural phase transition at low temperature to the tetragonal I4/m structure.