Twinned tetragonal structure and equation of state of NaTh2F9

The crystal structure and stability of NaTh₂F₉ have been studied using thermal analysis, powder X-ray diffraction at atmospheric conditions, and single-crystal X-ray diffraction at high pressure. Sodium dithorium fluoride is stable at least up to 5.0 GPa at room temperature and to 954 K at ambient pressure. In contrast to earlier investigations, which have reported the structure to be cubic (, Z=4), we observe a tetragonal distortion of the lattice. The actual crystal structure (, Z=4) is twinned and composed of corner-sharing distorted ThF₉ tricapped trigonal prisms and distorted NaF₆ octahedra. The twinning element is a three-fold axis from cubic symmetry. The ThF₉ polyhedra are rigid and it is the volume changes of the octahedra around the Na atoms that have the major contribution to the bulk compressibility. The zero-pressure bulk modulus B₀ and the unit-cell volume at ambient pressure V₀ are equal to 99(6) GPa and 663.1(1.0) Å³, respectively, with the fixed first pressure derivative of the bulk modulus B′=4.00. An inspection of the known crystalline phases in the system NaF-ThF₄ reveals that their bulk moduli increase with the increasing ThF₄ content.