Ultrasound assisted ambient temperature synthesis of ternary oxide AgMO2 (M=Fe, Ga)

The application of ultrasound for the synthesis of ternary oxide AgMO₂ (M=Fe, Ga) was investigated. Crystalline α-AgFeO₂ was obtained from the alkaline solutions of silver and iron hydroxides by sonication for 40 minutes. α-AgFeO₂ was found to absorb optical radiation in the 300-600 nm range as shown by diffuse reflectance spectroscopy. The Raman spectrum of α-AgFeO₂ exhibited two bands at 345 and 638 cm⁻¹. When β-NaFeO₂ was sonicated with aqueous silver nitrate solution for 60 minutes, β-AgFeO₂ possessing orthorhombic structure was obtained as the ion-exchanged product. The Raman spectrum of β-AgFeO₂ showed four strong bands at 295, 432, 630 and 690 cm⁻¹. Sonication of β-NaGaO₂ with aqueous silver nitrate solution for 60 minutes resulted in olive green colored, α-AgGaO₂. The diffuse reflectance spectrum and the EDX analysis confirmed that the ion-exchange through sonication was complete. The Raman spectrum of α-AgGaO₂ had weak bands at 471 and 650 cm⁻¹.