| 复合无机粘结剂对钌酸铋/银基厚膜电阻性能影响 |
| |
| 引用本文： | 郑晓慧,堵永国,张为军,芦玉峰,唐珍兰.复合无机粘结剂对钌酸铋/银基厚膜电阻性能影响[J].电子元件与材料,2005,24(10):23-26. |
| |
| 作者姓名： | 郑晓慧 堵永国 张为军 芦玉峰 唐珍兰 |
| |
| 作者单位： | 国防科学技术大学航天与材料工程学院,湖南,长沙,410073;国防科学技术大学航天与材料工程学院,湖南,长沙,410073;国防科学技术大学航天与材料工程学院,湖南,长沙,410073;国防科学技术大学航天与材料工程学院,湖南,长沙,410073;国防科学技术大学航天与材料工程学院,湖南,长沙,410073 |
| |
| 基金项目： | 国家高技术研究发展计划(863计划) |
| |
| 摘 要： | 采用钙铝硅玻璃和硼硅酸铅玻璃组成的复合体系作为无机粘结剂制备厚膜电阻浆料,研究复合无机粘结剂对厚膜电阻各性能的影响。结果表明,二组元在复合体系中体积分数的改变影响钌酸铅“过渡层”的存在状态和无机粘结剂中晶相和玻璃相的比例,使厚膜电阻的方阻和电阻温度系数随之变化,当二组元体积分数均为50%时,制备的电阻膜性能稳定,重烧变化率为2.7%。
|
| 关 键 词： | 无机非金属材料 厚膜电阻 复合体系 方阻 电阻温度系数 重烧特性 |
| 文章编号： | 1001-2028（2005）10-0023-04 |
| 收稿时间： | 2005-05-18 |
| 修稿时间： | 2005-05-18 |
Effect of Compound Inorganic Binder on Properties of Bismuth Ruthenate/Silver Based Thick-film Resistors |
| |
| ZHENG Xiao-hui,DU Yong-guo,ZHANG Wei-jun,LU Yu-feng,TANG Zhen-lan.Effect of Compound Inorganic Binder on Properties of Bismuth Ruthenate/Silver Based Thick-film Resistors[J].Electronic Components & Materials,2005,24(10):23-26. |
| |
| Authors: | ZHENG Xiao-hui DU Yong-guo ZHANG Wei-jun LU Yu-feng TANG Zhen-lan |
| |
| Institution: | National University of Defense Technology, Changsha 410073, China |
| |
| Abstract: | The mixture of calcium oxide-alumina-silicon dioxide(CaO-Al2O3-SiO2) glass and lead oxide-boron oxide-silicon dioxide(PbO-B2O3-SiO2) glass was used as inorganic binder to produce thick film pastes.Effect on properties of thick-film resistors was studied when inorganic binder phases were changed.It has been found that the change of ingredients of glass alters the form of lead ruthenate pyrochlore “transition layer” and the proportion between crystal phase and glass phase.The sheet resistivity and temperature coefficient of resistance are also influenced.When the ratio of the two glass is both 50 percent,thick-film resistors are stable and the refiring change ratio is 2.7 percent. |
| |
| Keywords: | inorganic non-metallic materials thick-film resistors compound system sheet resistivity temperature coefficient of resistance retiring character |