Hafnium oxide thin films deposited from a filtered cathodic vacuum arc

The electrical and structural characteristics of hafnium oxide thin films reactively deposited from a filtered cathodic vacuum arc have been investigated. X-ray photoelectron spectroscopy was used to determine the deposition conditions (Ar/O₂ ratio) which produced stoichiometric HfO₂ films. Cross-sectional transmission electron microscopy showed that the micro-structure of the films was highly disordered with electron-diffraction analysis providing evidence for the presence of sub-nano-metre crystallites of the monoclinic HfO₂ (P2₁/c) phase. Further evidence for the presence of this phase was provided by measuring the O k-edge using electron energy loss spectroscopy and comparing it with calculations performed using FEFF8.2, a multiple scattering code. Surface imaging revealed that local film damage occurred in films deposited with substrate bias voltages exceeding −200 V. The current-leakage characteristics of the HfO₂ films deposited with a bias of approximately −100 V suggest that device grade HfO₂ films can be produced from a filtered cathodic vacuum arc.