Synthesis and charge-discharge performance of Li5SiN3 as a cathode material of lithium secondary batteries

Li₅SiN₃ crystals are synthesized by direct reaction between Li₃N and Si₃N₄ with the molar ratio Li₃N/Si₃N₄ of 10:1. Reaction is performed at 1073 K for 1 h under a nitrogen atmosphere of 700 Torr. The lattice constant determined by the X-ray powder diffraction method is 4.718 Å. Four broad Raman peaks are observed at 196, 286, 580, and 750 cm^?1. By analogy with LiMgN, the broad peak at 580 cm^?1 with a half width of 140 cm^?1 is attributed to homogenously random distribution of Li and Si atoms. The band gap of Li₅SiN₃ is found to be a direct gap of about 2.5 eV by optical absorption and photoacoustic spectroscopy methods. Comparison with the conventional cathode materials for lithium ion batteries, this gap value is close to d-d transition energy of Mn in LiMn₂O₄ (1.63 eV or 2.00 eV) and that of Co in LiCoO₂ (2.1 eV), suggesting that Li₅SiN₃ is a possible cathode material. The 5 × 5 mm²-sized lithium secondary battery of Li₅SiN₃ cathode/propylene carbonate + LiClO₄ electrolyte/Li anode structure shows a discharge capacity of 2.4 μAh cm^?2 for a discharge current of 1.0 μA.