Thermoanalytical studies of 2,2,6,6-tetramethyl-4-oxy-4-ethynylpiperidin-1-oxyl polymerization

The structure transition temperature, monomer melting point and critical temperatures of polymerization and decomposition of 2,2,6,6-tetramethyl-4-oxy-4-ethynylpiperidin-1-oxyl were determined by means of thermal analysis. Some features of the polymerization of the acetylenic monomer were studied via thermal analysis, and IR and ESR spectroscopy.It was shown that, during non-isothermal temperature increase, the mass loss of the sample associated with the exothermic effect of polymerization occurred at the expense of the monoacetylene sublimation process (42%), a reagent explosion and decomposition of the reaction products formed (15%).

---

Zusammenfassung Mittels Thermoanalyse wurde die Strukturumwandlungstemperatur, der Monomerschmelzpunkt und die kritischen Temperaturen für Polymerisierung und Zersetzung von 2,2,6,6-Tetramethyl-4-oxy-4-ethynylpiperidin-1-oxyl bestimmt. Mit Hilfe von Thermo-analyse, IR- und ESR-Spektroskopie wurden einige Eigenschaften der Polymerisierung des Acethylen-Monomers untersucht.Es wurde gezeigt, daß bei einem nichtisothermen Temperaturanstieg der Massenverlust der Probe zunimmt, verbunden mit einem exothermen Effekt der eingetretenen Polymerisierung auf Kosten des Monoacetylen-Sublimierungsprozesses 42%], der Explosion und der Zersetzung der gebildeten Reaktionsprodukte 15%].