Preparation of Chitosan/Polyvinyl Alcohol Electrospinning Nano-Membranes Using the Green Solvent,Plasma Acid |
| |
Authors: | Ying Wang Jia-qing Wu Qian Wan Lei Zhang Hong-na Lei |
| |
Institution: | 1. School of Textile and Material Engineering, Dalian Polytechnic University, Dalian, Chinawangying@dlpu.edu.cn;3. School of Textile and Material Engineering, Dalian Polytechnic University, Dalian, China |
| |
Abstract: | AbstractIn this paper, a green solvent for chitosan, plasma acid, was made and chitosan/plasma-acid solutions were prepared. An environmentally friendly chitosan/polyvinyl alcohol (PVA) nano-membrane was prepared via electrospinning due to the difficulty of electrospinning of pure chitosan/plasma-acid solutions. Two blending methods of chitosan with PVA were investigated. One way was to mix a chitosan/plasma-acid solution (1%) and a PVA/water solution (10%) with the volume ratios of 2:8, 3:7, 4:6, 5:5, 6:4, 7:3 and 8:2, respectively. The results showed that fibrous nano-membranes could start to be formed at a chitosan/PVA mixing ratio of 7:3 up to the ratio of 2:8 with increasing PVA. The average fiber diameters increased with increased adding of PVA, ranging from 74.7?nm for the 7:3 ratio to 280.7?nm for the 2:8 ratio. The other way to prepare the chitosan/PVA solutions was to put PVA and chitosan powders into the plasma acid together. Fibrous nano-membranes could also be formed at 6% PVA and 10% PVA solution, both with 1% chitosan compositions. The average diameters of the resulting nano-fibers were 144.67?nm and 300.7?nm, respectively. The Fourier transform infrared (FTIR) spectroscopy results showed that the chitosan was bonded to the PVA by hydrogen bonds in the nano-membranes (6% PVA, 1% chitosan). It is noted that both of the two blending methods permitted obtaining chitosan/PVA nano-membranes. As indicated, the PVA in the solution had a large effect on the diameters of the nano-fibers. The first method permitted obtaining nano-fibers with smaller diameter. The maximum concentration of chitosan in the solution was 0.7% (7:3 ratio). The second method was simpler and permitted increasing the chitosan concentration in the solution to 1% for both the 6% and 10% concentrations of PVA. |
| |
Keywords: | chitosan electrospinning nano-membrane plasma acid PVA |
|
|