Effect of annealing on thermal properties and crystalline structure of polyamides. Nylon 11 (polyundecaneamide) |
| |
Authors: | Doz Dr hab S Gogolewski |
| |
Institution: | (1) Technical University, Laboratory of Polymers, Podgorna 50, PL-65-246 Zielona Gora, Poland |
| |
Abstract: | Summary The effect of prolonged annealing at a low super-cooling on the thermal properties and crystalline structure of nylon 11 has been investigated. Annealed nylon 11 formed the lamellar spherulites of the alpha-crystalline modification. Thickness of the lamellae increased with time of annealing from 50 to 165 Å for the samples annealed for 20 and 2000 hours respectively. Corresponding values of the melting temperature and the heat of melting increased from 190 °C and 10 cal/g to 211 °C and 20 cal/g.The extrapolated heat of melting of the crystalline phase of nylon 11 is 47 cal/g.
Zusammenfassung Untersucht wurden die thermischen Eigenschaften und kristallinen Strukturen des 11-Polyamid nach langfristiger Temperung mit Temperaturen nahe dem Schmelzpunkt.Getempertes 11-Polyamid bildete lamellenartige Sphärolithe und kristallisiert in alpha-Modifikation.Die Dicke der Lamellen vergrößert sich mit der Temperungszeit von 50 Å bei einer Temperungszeit von 20 Stdn. bis auf 165 Å bei einer Zeit von 2000 Stdn.Schmelzpunkt und Schmelzwärme dieser getemperten Proben erhöhen sich entsprechend von 190 °C und 10 cal/g auf 211 °C und 20 cal/g.Die extrapolierte Schmelzwärme der kristallinen Phase von 11-Polyamid beträgt 47 cal/g.
With 8 figures Presented in part at the 8th Europhysics Conference on Macromolecular Physics, Bristol, 1978. |
| |