Glass formation in and structural investigation of Li2S + GeS2 + GeO2 composition using Raman and IR spectroscopy

Li₂S + GeS₂ + GeO₂ ternary glasses have been prepared and a wide glass-forming range was obtained. The glass transition temperatures increase with the GeO₂ concentration in the glasses. The vibrational modes of both bridging (Ge–S–Ge) and non-bridging (Ge–S^?) sulfurs are observed in Raman and IR spectra of binary Li₂S + GeS₂ glasses. Additions of GeO₂ to this binary glass increase the bridging oxygen band (Ge–O–Ge) at the expense of decreasing the bridging sulfur band (Ge–S–Ge), whereas the bands associated with the non-bridging sulfurs (Ge–S^?) remain constant in intensity up to high GeO₂ concentrations. At higher concentrations of GeO₂ (?60%), the non-bridging oxygen band, which is not observed at low and intermediate GeO₂ concentrations, appears and grows stronger. From these observations, it is suggested that the added lithium ions favor the non-bridging sulfur sites over the oxygen sites to form non-bridging sulfurs, whereas the added oxygen prefers the higher field strength Ge⁴⁺ cation to form bridging Ge–O–Ge bonds. The structural groups in the Li₂S + GeS₂ + GeO₂ glasses that are consistent with results of Raman and IR spectra are described and are used to develop a structural model of these glasses.