Emission features of Ho ion in Nb2O5, Ta2O5 and La2O3 mixed Li2O-ZrO2-SiO2 glasses

Li₂O-ZrO₂-SiO₂: Ho³⁺ glasses mixed with three interesting d-block elemental oxides, viz., Nb₂O₅, Ta₂O₅ and La₂O₃, were prepared. Optical absorption and photoluminescence spectra of these glasses have been recorded at room temperature. The luminescence spectra of Nb₂O₅ and Ta₂O₅ mixed Li₂O-ZrO₂-SiO₂ glasses (free of Ho³⁺ ions) have also exhibited broad emission band in the blue region. This band is attributed to radiative recombination of self-trapped excitons (STEs) localized on substitutionally positioned octahedral Ta⁵⁺ and Nb⁵⁺ ions in the glass network. The Judd-Ofelt theory was successfully applied to characterize Ho³⁺ spectra of all the three glasses. From this theory various radiative properties, like transition probability A, branching ratio β_r and the radiative lifetime τ_r, for ⁵S₂ emission levels in the spectra of these glasses have been evaluated. The radiative lifetime for ⁵S₂ level of Ho³⁺ ions has also been measured and quantum efficiencies were estimated. Among the three glasses studied the La₂O₃ mixed glass exhibited the highest quantum efficiency. The reasons for such higher value have been discussed based on the relationship between the structural modifications taking place around the Ho³⁺ ions.