Synthesis of pH‐responsive magnetic yolk–shell nanoparticles: A comparison between conventional etching and new deswelling approaches

Iron oxide (Fe₃O₄) magnetic nanoparticles as movable cores were used to synthesize yolk–shell nanoparticles with pH‐responsive shell composed of ethylene glycol dimethacrylate (EGDMA)‐crosslinked poly(acrylic acid) (PAA) via two different routes. In the first more common route, Fe₃O₄ nanoparticles were coated with silica layer via the Stöber process to yield Fe₃O₄@SiO₂ core–shell nanoparticles, subsequently used as seeds in the distillation precipitation copolymerization of AA and EGDMA to yield Fe₃O₄@SiO₂@P(AA‐EGDMA). The silica layer was selectively removed through alkali etching to yield Fe₃O₄@air@P(AA‐EGDMA). In the second route, Fe₃O₄ nanoparticles without any stabilization were used as seeds in the distillation precipitation copolymerization of AA and EGDMA to yield Fe₃O₄@P(AA‐EGDMA) core–shell nanoparticles. The nanoparticles were subsequently dispersed in acidic medium of pH = 2. Yolk–shell Fe₃O₄@air@P(AA‐EGDMA) nanoparticles were formed through deswelling of crosslinked PAA because of protonation of carboxyl groups at low pH values. Various techniques were utilized to investigate the characteristics of the synthesized core–shell nanoparticles. Formation of yolk–shell nanostructure was observed for both synthesis routes, namely etching of silica layer and deswelling approaches, from vibrating sample magnetometry and transmission electron microscopy results. Both types of nanoparticles showed pH‐responsive behaviour, i.e. decrease in absorption with increase in pH, as examined using UV–visible spectroscopy.