| Abstract: | The crystal structure produced during the isothermal crystallization of polyethylene (PE) copolymers with a broad range of comonomer concentrations was determined by the measurement of the melting endotherms directly after crystallization. PE copolymers with higher concentrations of short‐chain branches (≥10 branches per 1000 total carbon atoms) exhibited strong resistance to crystal thickening during isothermal crystallization. Negligible thickening, estimated to be only about 0.1 nm in 10 min of isothermal crystallization, was observed. The side‐chain branches apparently acted as limiting points of chain incorporation into the crystals, which exhibited great resistance to the modification of their position, that is, crystal thickening. Even with long periods (up to 8 h) of isothermal storage, crystal thickening was very small or negligible, about 0.3 nm. The crystal thickness was calculated from differential scanning calorimetry data. The behavior of copolymers with lower branching concentrations and the unbranched PE homopolymer was quite different from that of the copolymers with higher branching. Polymers with low or no branching exhibited the initial crystallization of a thinner crystal population, which thickened substantially with increasing time. The thickening observed for these lower or unbranched polymers was an order of magnitude larger, that is, 1.6–2.0 nm in 10 min of isothermal crystallization. Copolymers with higher concentrations of branching had relatively short sequence lengths of ethylene units between branch points, and this resulted in strong control over the crystal thickness by the branch points and great resistance to crystal thickening, even with long times of isothermal crystallization. Copolymers with low concentrations of branching had relatively long sequence lengths of ethylene units between branch points, and this resulted in little control over the crystal thickness by the branch points and rapid crystal thickening upon isothermal crystallization. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 235–246, 2003 |