Mesoporous structures in never-dried softwood cellulose fibers investigated by nitrogen adsorption

Nitrogen adsorption was used to characterize mesoporous structures in never-dried softwood cellulose fibers. Distinct inflections in desorption isotherms were observed over the relative vapor pressure (P/P₀) range of 0.5–0.42 for never-dried cellulose fibers and partially delignified softwood powders. The reduction in N₂ adsorption volume was attributed to cavitation of condensed N₂ present in mesopores formed via lignin removal from wood cell walls during delignification. The specific surface areas of significantly delignified softwood powders were ~150 m² g^?1, indicating that in wood cell walls 16 individual cellulose microfibrils, each 3–4 nm in width, form one cellulose fibril bundle surrounded with a thin layer of lignin and hemicelluloses. Analysis of N₂ adsorption isotherms indicates that mesopores in the softwood cellulose fibers and partially delignified softwood powders had peaks ranging from 4 to 20 nm in diameter.