Radiation response behaviour of Al codoped germano-silicate SM fiber at high radiation dose |
| |
Authors: | M.C. Paul R. Sen S.K. Bhadra K. Dasgupta |
| |
Affiliation: | Fiber Optics Division, Central Glass and Ceramic Research Institute, 196, Raja S.C. Mullick Road, Kolkata 700 032, India |
| |
Abstract: | Radiation response behaviour of Ge + Al doped SM fiber fabricated by the solution doping process has been studied at room temperature with respect to 1310 nm transmission wavelength under three different dose rates of 200, 400 and 600 Rad/min to compare with that of standard Er doped as well as Ge doped SM fibers. Their radiation sensitivity has been observed with variation of dose rates, transmission wavelength along with their recovery nature. Radiation response behaviour of Al doped SM fiber is found to be slightly non-linear in nature with very low dose rate dependency. No saturation level was found upto 13 Krad cumulative dose. Thermobleaching as well as photobleaching phenomena have also been studied. Gamma irradiated Al doped preform shows an absorption peak at around 300 nm due to generation of Al (E′) defect center and gets annihilated after thermobleaching process. Gamma irradiated Al doped SM fiber shows prominent photobleaching effect on their optical attenuation with respect to the 850 nm transmission wavelength. From ESR study resonance signals for Al3+ related radiation-induced defect centers are not clearly observed in this study. A very weak hyperfine pattern has been observed for gamma irradiated Al doped preform sample. The high radiation sensitivity along with linear response behaviour, low recovery and almost dose rate independence behaviour of the material system of Ge + Al codoped SM core optical fiber under gamma radiation shows their potential for application as fiber optic radiation sensor in comparison to the universal standard erbium doped SM fiber. |
| |
Keywords: | 42.81 42.88 78.40.F,H 42.70.C 42.81.P |
本文献已被 ScienceDirect 等数据库收录! |
|