Pr3+,Yb3+共掺YPO4下转换材料的制备及其转光效率
引用本文:李开宇,王如志,曲铭浩,张影,严辉.Pr3+,Yb3+共掺YPO4下转换材料的制备及其转光效率[J].发光学报,2012,33(5):486-491.
作者姓名:李开宇  王如志  曲铭浩  张影  严辉
作者单位:北京工业大学 材料科学与工程学院, 北京 100124
基金项目:国家自然科学基金,北京市“学术创新团队建设计划”项目,北京市科技新星计划,北京市自然科学基金,北京工业大学基础研究基金资助项目
摘    要:采用固相反应法制备了Pr3+,Yb3+共掺杂的YPO4下转换发光粉体,并在450 nm光激发条件下,研究了Yb3+不同摩尔分数(0%,1%,2%,4%,20%,30%)对转光效率的影响。结果表明:不同Yb3+浓度的样品,其荧光峰强度不同,这可能是由于Pr3+-Yb3+之间Yb3+浓度不同存在能量传递效率差异的原因。研究也发现了样品的下转换发光,其能量传递过程为:Pr3+:3P0→Yb3+:2F5/2+2F5/2。荧光光谱测试结果表明,Yb3+的最佳掺杂摩尔分数为2%。Pr3+,Yb3+共掺杂的YPO4材料在提高太阳能电池光电转换效率方面具有潜在的应用。

关 键 词:下转换  稀土离子  YPO4  太阳能电池
收稿时间:2012/1/20

Downconversion Materials Preparation and The Research of Conversion Efficiency in Pr3+ , Yb3+ Co-doped YPO4
LI Kai-yu , WANG Ru-zhi , QU Ming-hao , ZHANG Ying , YAN Hui.Downconversion Materials Preparation and The Research of Conversion Efficiency in Pr3+ , Yb3+ Co-doped YPO4[J].Chinese Journal of Luminescence,2012,33(5):486-491.
Authors:LI Kai-yu  WANG Ru-zhi  QU Ming-hao  ZHANG Ying  YAN Hui
Institution:College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
Abstract:Pr3+,Yb3+ co-doped YPO4 downconversion phosphor powders were prepared by solid state reaction.When excitation at 450 nm,the effects of different Yb3+ mole fractions(0%,1%,2%,4%,20%,30%) on the conversion efficiency are studied.Results shows that because of the difference of energy transfer efficiency between Pr3+ and Yb3+,the samples with various Yb3+ doping concentrations have different fluorescence intensity.It is also found that the energy transfer process of the downconversion luminescence in samples is Pr3+:3P0→Yb3+:2F5/2+2F5/2.From photoluminescence spectra measurement,the optimal doping mole fraction of Yb3+ is 2%.The results indicate that Pr3+,Yb3+ co-doped YPO4 downconversion phosphor is a kind of potential material which may be used to improve the solar cell efficency.
Keywords:downconversion  rare earth  YPO4  solar cells