Synthesis, Structures, and Thermal Expansion of the La2W2−xMoxO9 Series

The La₂W_2−xMo_xO₉ series has been synthesized by the ceramic method. An alternative synthesis using microwave radiation is also reported. La₂W₂O₉ has two polymorphs and the low-temperature phase (α) transforms to the high-temperature form (β) at 1077°C. The influence of the W/Mo substitution in this phase transition has been investigated by DTA. The β structure for x≥0.7 compositions can be prepared as single phase at any cooling rate. The β phase for 0.3≤x≤0.7 compounds can be prepared as single phase by quenching, whereas a mixture of α and β phases is obtained by slow cooling. The W/Mo ratio in both coexisting phases is different with the β-phase having a higher Mo content. The x=0.1 and 0.2 compounds have been prepared as mixtures of phases. The room temperature structure of β-La₂W_1.7Mo_0.3O₉ has been analyzed by the Rietveld method in P2₁3 space group. The final R-factors were R_WP=9.0% and R_F=5.6% with a structure similar to that of β-La₂Mo₂O₉. Finally, the thermal expansion of both types of structures has been determined from a thermodiffractometric study. The thermal expansion coefficients were 2.9×10⁻⁶ and 9.7×10⁻⁶°C⁻¹ for α-La₂W₂O₉ and β-La₂W_1.2Mo_0.8O₉, respectively.