Reactivity and Structural Properties of a Mechanochemically Treated Ag2O-V2O5 System in Relation to AgVO3 Polymorphs

Formation and chemical properties of amorphous AgVO₃, which was prepared by mechanochemical treatment of an Ag₂O-V₂O₅ mixture, and crystalline AgVO₃ were studied in relation to AgVO₃ polymorphs. A ball-milled sample of the mixture was assigned as a highly deformed β-AgVO₃ rather than the low density phase α-AgVO₃. Crystalline α-AgVO₃ and β-AgVO₃ were converted into deformed β-AgVO₃ by ball milling, which produced a clear change. δ-AgVO₃ is resistant to mechanical treatment and its structure was not markedly affected. The dissolved chemical species from the ball-milled sample precipitates to form α-AgVO₃ without a seeding crystal, but other polymorphs deposit if they are present; i.e., β-AgVO₃ and δ-AgVO₃ grow on the seeding crystal.