XRD, conductivity and FTIR studies on LiI-Li2WO4-Li3PO4 prepared by low temperature sintering

Different amounts of Li₃PO₄ were mixed to a fixed ratio of LiI:Li₂WO₄, ground and pelletised before subjected to sintering at 70°C for 7 days. XRD shows that the product formed after sintering process is most likely Li₆P₄W₈O₃₂ due to peaks present at 10.6°, 22.4°, 24.0°, 24.4, 26.2°, 32.4° and 34.0°. Conductivity studies show that the sample with 25 wt.% Li₃PO₄ exhibits the highest room temperature conductivity of 3.42×10⁻³ Scm⁻¹. Conductivity is expected to occur through channel-like structures which could have formed due to corner or edge sharing of polyhedra. FTIR studies have shown the existence of WO₄ tetrahedra and WO₆ octahedral at 850 cm⁻¹ and 952 cm⁻¹, and phosphate tetrahedral at 564 cm⁻¹, 700 cm⁻¹, 890 cm⁻¹ and 1030 cm⁻¹.