High pressure synthesis of the mixed valent and nonsuperconducting ternary YbRhxSny compound

The ternary compound YbRh_1.4Sn_4.6 with the phase I structure (simple cubic) when subjected to a pressure of 40 kbar at 800°C is found to transform to phase III structure (f.c.c.) with the composition YbRh_1.1Sn₃. The latter compound has a lattice parameter of $\text{a = 13.735}\text{A}\text{?}$ which suggests that the Yb is in an intermediate valence state. The temperature dependence of magnetic susceptibility suggests that the Yb is in a homogeneously mixed valence state in the pressure synthesized product. In the phase I structure YbRh_1.1Sn_4.6 is superconducting at 8.6°K, but in the phase III structure the compound YbRh_1.1Sn₃ is not superconducting down to 0.9°K. It is suggested that superconductivity and mixed valence are incompatible.