| 掺钯碳纳米管的制备及电接触性能 |
| |
| 引用本文： | 孙蒙蒙,常春蕊,张志明,安立宝.掺钯碳纳米管的制备及电接触性能[J].高等学校化学学报,2019,40(1):11. |
| |
| 作者姓名： | 孙蒙蒙 常春蕊 张志明 安立宝 |
| |
| 作者单位： | 1. 华北理工大学机械工程学院, 河北省无机非金属材料重点实验室, 2. 理学院, 3. 材料科学与工程学院, 唐山市功能高分子材料重点实验室, 唐山 063210 |
| |
| 基金项目： | 国家自然科学基金(批准号: 51472074)和河北省“百人计划”项目(批准号: E2012100005)资助. |
| |
| 摘 要： | 以PbCl2为介质, 采用无电沉积方法制备了掺钯碳纳米管, 并对其形貌和结构进行了表征. 结果表明, 掺入的钯纳米粒子分布均匀、 粒径均一, 掺杂量与粒径尺寸适中; 所掺入的纳米粒子的成分为0价态的钯, 且掺杂类型为p型. 电接触性能测试结果表明, 掺钯碳纳米管与金电极间的接触电阻得到了明显改善, 阻值平均降幅高达近71.09%.
|
| 关 键 词： | 多壁碳纳米管 掺杂 无电沉积 钯纳米粒子 接触电阻 |
| 收稿时间： | 2018-07-17 |
Preparation and Electrical Contact Properties of Palladium-doped Multi-walled Carbon Nanotubes† |
| |
| SUN Mengmeng,CHANG Chunrui,ZHANG Zhiming,AN Libao.Preparation and Electrical Contact Properties of Palladium-doped Multi-walled Carbon Nanotubes†[J].Chemical Research In Chinese Universities,2019,40(1):11. |
| |
| Authors: | SUN Mengmeng CHANG Chunrui ZHANG Zhiming AN Libao |
| |
| Institution: | 1. Hebei Provincial Key Laboratory of Inorganic Nonmetallic Materials, College of Mechanical Engineering, 2. College of Sciences, 3. College of Material Science and Engineering, Key Laboratory of Functional PolymerMaterials of Tangshan, North China University of Science and Technology, Tangshan 063210, China |
| |
| Abstract: | Multi-walled carbon nanotubes(MWCNTs) were oxidized by mixed acid, and immersed into the electroless deposition solution of palladium. After ultrasonicating, resting, and stirring respectively for 5 or 10 min, palladium-doped MWCNTs were prepared, and their morphology and structure were characte-rized. The results showed that the nanoparticles were uniformly distributed onto the MWCNTs with uniform and moderate particle size and doping amount after 5 min of stirring. At the same time, the composition of the doped nanoparticles was detected as zero-valent palladium and the doping type was p-type. In the electrical contact performance test, the contact resistance between the palladium-doped CNTs and the gold electrode was significantly improved, and the average value of the resistance decreased by nearly 71.09%. |
| |
| Keywords: | Multi-walled carbon nanotubes Doping Electroless deposition Palladium nanoparticles Contact resistance |
|