| Abstract: | The α to γ transition that occurs in nylon 6 upon iodine treatment was investigated by infrared spectroscopy, differential thermal analysis, and x-ray diffraction techniques. Thin films of nylon (0.2 mil) were treated in either iodine–potassium iodide aqueous solution or in iodine vapor. Very short treatment times, in the order of 30 sec, were found to effect the transition when a solution 0.5M with respect to iodine was used. The infrared spectra of the iodine nylon complexes formed from either the α- or γ-nylon 6 treated in vapor or dissolved iodine were all similar. This is an indication that molecular iodine is the active species in forming the complex. The temperature of the washing solution used to remove the iodine from the nylon determines whether an α-nylon 6 or γ-nylon 6 is obtained from the complex after washing. Nylon 6 plaque surfaces and thin films are similar in their behavior towards the iodine treatment. The γ-nylon 6 is a stable modification at all temperatures below its melting point. The conversion of the γ form back to the α modification can occur only if the hydrogen bonding is severely affected, e.g., by phenol treatment, iodine treatment, melting, etc. Infrared spectroscopy provided no evidence for an α–γ transition in nylon 6 on heating the sample continuously through its melting point. The shapes of the melting peaks in the above two modifications of nylon 6 were sufficiently different to provide a means of identifying the two crystalline forms. |