Reduction of Cu2+ to Cu+ in Xerogels Prepared from (3-Aminopropyl)Trimethoxysilane

Silica gels doped with Cu²⁺ ions were prepared from the (3-aminopropyl) trimethoxysilane (APTMOS)/tetraethoxysilane (TEOS) systems. Sols showed a broad absorption peak at 640 nm, suggesting 3–5 coordination of the aminopropyl groups to Cu²⁺. For gels prepared from APTMOS and dried at room temperature, the 640 nm peak decreased and a red-shifted absorption appeared below 400 nm within a few months. The luminescence spectra of the xerogels showed emission bands at 430–470 and 510 nm. The former and latter bands are ascribed to Cu⁺ monomer and dimer emissions, respectively. These results indicate that Cu²⁺ ions are reduced to Cu⁺. When xerogels were prepared from APTMOS/TEOS = 1 (vol/vol), the color of xerogels was blue with an absorption peak at around 670 nm, indicating no reduction of Cu²⁺ ions.