Magnetic properties and charge ordering in Pr0.75Na0.25MnO3 manganite |
|
| Authors: | X.H. Zhang Z.Q. Li W. Song P. Wu H.L. Bai E.Y. Jiang |
| Affiliation: | a Institute of Advanced Materials Physics, Faculty of Science, Tianjin University, Tianjin 300072, China b Tianjin Key laboratory of Low Dimensional Materials Physics and Preparing Technology, Tianjin University, Tianjin 300072, China c Analysis Center, Tianjin University, Tianjin 300072, China d School of Material Science and Engineering, Tianjin University, Tianjin 300072, China |
| Abstract: | The structural and magnetic properties of Pr0.75Na0.25MnO3 have been investigated experimentally. At room temperature, the compound shows paramagnetic characteristic. Along with decreasing temperature, a peak appears in the magnetization versus temperature curve around 220 K. To clarify whether this peak is associated with the ordering arrangement of Mn3+ and Mn4+ ions, electron diffraction experiments were carried out below and above 220 K respectively. Only basic Brag diffraction spots can be observed at high temperatures, however, superlattice diffraction appears below 220 K. This provides direct evidence for the existence of charge ordering in Pr0.75Na0.25MnO3. We find the Mn3+ and Mn4+ cations form zigzag chains in a-c plane by analyzing the diffraction patterns. Combining with the magnetization measurements and the results of electron spin resonance, we confirm the antiferromagnetic phase and ferromagnetic component coexist in Pr0.75Na0.25MnO3 below 120 K. |
| Keywords: | 75.47.Lx 75.47.Gk 75.30.Kz |
| 本文献已被 ScienceDirect 等数据库收录！ | |