Improvement of the magnetic properties of barium hexaferrite nanopowders using modified co-precipitation method

Barium hexaferrite BaFe₁₂O₁₉ powders have been synthesized using the modified co-precipitation method. Modification was performed via the ultrasonication of the precipitated precursors at room temperature for 1 h and the additions of the 2% KNO₃, surface active agents and oxalic acid. The results revealed that single phase magnetic barium hexaferrite was formed at a low annealing temperature of 800 °C for 2 h with the Fe³⁺/Ba²⁺ molar ratio 8. The microstructure of the powders appeared as a homogeneous hexagonal platelet-like structure using 2% KNO₃ as the crystal modifier. A saturation magnetization (60.4 emu/g) was achieved for the BaFe₁₂O₁₉ phase formed at 1000 °C for 2 h with Fe³⁺/Ba²⁺ molar ratio 8 using 5 M NaOH solution at pH 10 in the presence of 2% KNO₃. Moreover, the saturation magnetization was 52.2 emu/g for the precipitated precursor at Fe³⁺/Ba²⁺ molar ratio 12 in was achieved for the precipitated precursor ultrasonicated for 1 h and then annealed at 1200 °C for 2 h. Coercivities from 956.9 to 4558 Oe were obtained at different synthesis conditions.