Benzoxazine-bismaleimide blends: Curing and thermal properties

A blend of bisphenol A based benzoxazine (Bz-A) and a bismaleimide (2,2-bis4(4-maleimidophenoxy) phenyl] propane (BMI), was thermally polymerised in varying proportions and their cure and thermal characteristics were investigated. The differential scanning calorimetric analysis, supplemented by rheology confirmed a lowering of the cure temperature of BMI in the blend implying catalysis of the maleimide polymerisation by benzoxazine. FTIR studies provided evidences for the H-bonding between carbonyl group of BMI and -OH group of polybenzoxazine in the cured matrix. The cured matrix manifested a dual phase behaviour in SEM and DMTA with the minor phase constituted by polybenzoxazine dispersed in an interpenetrating polymer network (IPN) of polybenzoxazine and cured BMI. The IPN possessed improved thermal stability over the constituent polybenzoxazine. A benzoxazine monomer possessing allyl functional groups, 2,2′-bis(8-allyl-3-phenyl-3,4-dihydro-2H-1,3-benzoxazinyl) propane (Bz-allyl) was reactively blended with the same bismaleimide in varying stoichiometric ratios (Bz-allyl/BMI), where the curing involved mainly Alder-ene reaction between allyl- and maleimides groups and ring-opening polymerisation of benzoxazine. The rheological analysis showed the absence of catalytic polymerisation of BMI in this case. The overall processing temperature was lowered in the blend owing to the co-reaction of the two systems to form a single-phase matrix. The cured resins of both Bz-A/BMI and Bz-allyl/BMI blends exhibited better thermal stability than the respective polybenzoxazines. The T_g of the IPN was significantly improved over that of polybenzoxazine (Bz-A). However, the co-reaction resulted in a marginal decrease in the T_g of the system in comparison to the polybenzoxazine (Bz-allyl).