Engineering the Mesopores of Fe3O4@Mesosilica Core–Shell Nanospheres through a Solvothermal Post‐Treatment Method

A solvothermal post‐treatment method was developed to synthesize Fe₃O₄@mesosilica core–shell nanospheres (CSNs) with a well‐preserved morphology, mesoporous structure, and tunable large pore diameters (2.5–17.6 nm) for the first time. N,N‐Dimethylhexadecylamine (DMHA), which was generated in situ during the heat‐treatment process, was mainly responsible for this pore‐size enlargement, as characterized by NMR spectroscopy. This pore‐size expansion can be strengthened with the aid of hexamethyldisilazane (HMDS), whilst the nature of the surface of the Fe₃O₄@mesosilica CSNs can be easily modified with trimethylsilyl groups during the pore‐size‐expansion process. The hydrophobicity of the Fe₃O₄@mesosilica CSNs increased for the enlarged mesopores and the adsorption capacity of these CSNs for benzene (up to 1.5 g g^?1) is the highest ever reported for Fe₃O₄@mesosilica CSNs. The resultant Fe₃O₄@mesosilica CSNs (pore size: 10 nm) showed a 3.6‐times higher adsorption capacity of lysozyme than those without the pore expansion (pore size: 2.5 nm), thus making them a good candidate for loading large molecules.