Electrorheology and characterization of acrylic rubber and lead titanate composite materials

Oxide one‐pot synthesis was used to synthesize a polymer precursor to lead titanate, PbTiO₃. Perovskite lead titanate, PbTiO₃, was synthesized via the sol–gel process. The dielectric constant, electrical conductivity and loss tangent of our acrylic rubber (AR71)–lead titanate (PT) composite material (AR/PT_8) were 14.15, 2.62 × 10^?7/Ω m, and 0.093, respectively, measured at 27 °C and 1000 Hz. SEM micrographs of composites between the AR71 elastomer and PbTiO₃ showed that the particles were reinforced within the matrix. The electrorheological properties of the AR71/PT composites were investigated as functions of electric field strength from 0 to 2 kV/mm and PbTiO₃ particle volume fraction. The storage modulus increased linearly with particle volume fraction, with or without an electric field. Without an electric field, the particles merely acted as a filler to absorb or store additional stress. With the electric field on, particle‐induced dipole moments were generated, leading to interparticle interactions, and thus a substantial increase in storage modulus. With PbTiO₃ particle volume fractions as small as 10^?4 embedded in the elastomer matrix, the modulus increased by nearly a factor of 2 as the electric field strength varied from 0 to 2 kV/mm. Copyright © 2008 John Wiley & Sons, Ltd.