Electrical and mechanical properties of proton conducting SrCe0.95Yb0.05O3 − α

Yb³⁺-doped ceramic strontium cerate of exactly the composition SrCe_0.95Yb_0.05O_{3 − α} was prepared, having a relative density of 99.0 (± 0.3%). Great care was taken to obtain homogeneous, carbonate free material. Analysis are made of the X-ray powder diffraction pattern of the as-prepared dense ceramic, resulting in the orthorhombic unit cell parameters a = 6.997(2) Å, b = 12.296(3) Å, c = 8.588(2) Å, Z = 8 and d_x = 5.806(2) g cm⁻³. Bending strength values of the ceramic in non-proton and proton conducting state are found to be 177 and 194 MPa respectively. The ceramic kept under proton conducting conditions for 500 h at 300 °C to 800 °C in a N₂ flow containing 155 mbar water vapour and 245 mbar H₂, have shown to remain chemically and structurally stable. Impedance spectroscopy measurements of the bulk conductivity of the proton conducting ceramic revealed an activation energy of 53.2 kJ mol⁻¹ and a preexponential factor of 359.1 (Ω cm)⁻¹ K. In the non-proton conducting state the ceramic is mainly oxygen ion vacancy conducting, which indicates that charge compensation on substituting Yb⁺³ in SrCeO₃ takes place by oxygen ion vacancies.