| 凹凸棒黏土-SnO2-TiO2复合材料的制备及其光催化性能 |
| |
| 引用本文： | 张莉莉,吕伏建,刘建全,汤超,汪信.凹凸棒黏土-SnO2-TiO2复合材料的制备及其光催化性能[J].应用化学,2010,27(1):63-68. |
| |
| 作者姓名： | 张莉莉 吕伏建 刘建全 汤超 汪信 |
| |
| 作者单位： | (1.江苏省低维材料重点建设实验室，淮阴师范学院 淮安；2.南京理工大学材料化学实验室 南京 210097) |
| |
| 基金项目： | 江苏省高校科研成果产业化推进项目，江苏省教育厅自然科学基金，中国博士后科学基金，江苏省博士后基金，淮安市科技项目，淮阴师范学院大学生创新训练计划 |
| |
| 摘 要： | 以凹凸棒黏土为基体，通过原位溶胶-凝胶包覆工艺，将SnO2-TiO2复合氧化物负载于凹凸棒黏土表面制备凹凸棒黏土复合光催化剂(Att-SnO2-TiO2)。采用XRD、BET、TEM等分析测试技术对产物进行了表征。结果表明，SnO2-TiO2复合氧化物均匀地负载于凹凸棒黏土表面，其平均粒径约为10 nm；经过复合氧化物负载改性后，凹凸棒黏土的表面形貌得到明显改善，产物的包覆效果好、比表面大。以光催化降解甲基橙为探针，研究了凹凸棒黏土复合光催化剂的光催化性能。结果表明,凹凸棒黏土复合光催化剂显示出优异的光催化性能，其光催化活性顺序为Att-SnO2-TiO2>Att-SnO2>Att-TiO2。以性能最佳的Att-SnO2-TiO2为催化剂光降解甲基橙30min后，甲基橙的降解率达99%。实验表明，Att-SnO2-TiO2复合光催化剂可重复利用。
|
| 关 键 词： | SnO2-TiO2 光催化 凹凸棒黏土 负载 溶胶-凝胶 |
| 收稿时间： | 2009-01-04 |
| 修稿时间： | 2009-05-04 |
Synthesis of Attapulgite-SnO2-TiO2 Nanocomposites and Their Photocatalytic Property |
| |
| ZHANG Li-Li,LV Fu-Jian,LIU Jian-Quan,TANG Chao,WANG Xin.Synthesis of Attapulgite-SnO2-TiO2 Nanocomposites and Their Photocatalytic Property[J].Chinese Journal of Applied Chemistry,2010,27(1):63-68. |
| |
| Authors: | ZHANG Li-Li LV Fu-Jian LIU Jian-Quan TANG Chao WANG Xin |
| |
| Institution: | (1.aJiangsu Key Laboratory for Chemistry of Low Dimensional materials,Huaiyin Normal University,Huai′an;2.Nanjing University of Science and Technology,Nanjing 210094) |
| |
| Abstract: | Attapulgite(Att) was used as the matrix of SnO_2-TiO_2 hybrid oxide to synthesize a novel kind of composite photocatalyst(Att-SnO_2-TiO_2) by depositing SnO_2-TiO_2 hybrid oxides on the surface of Att via an in stiu sol-gel technique.The obtained products were characterized by means of X-ray diffraction(XRD),BET surface area and transmission electron microscope(TEM).Experimental results show that the surface of attapulgite was evenly covered by SnO_2-TiO_2 nanocomposites with particle size around 10 nm.The ... |
| |
| Keywords: | SnO_2-TiO_2 SnO~(2-)TiO_2 photocatalyst attapulgite loading sol-gel technique |