One‐pot synthesis of a new high vinyl content hybrid silica monolith dedicated to nanoliquid chromatography

A new vinyltrimethoxysilane‐based hybrid silica monolith was developed and used as a reversed‐phase capillary column. The synthesis of this rich vinyl hybrid macroporous monolith, by cocondensation of vinyltrimethoxysilane with tetramethoxysilane, was investigated using an unconventional (formamide, nitric acid) porogen/catalyst system. A macroporous hybrid silica monolith with 80% in mass of vinyltrimethoxysilane in the feeding silane solution was obtained and compared to a more conventional low vinyl content hybrid monolith with only of 20% vinyltrimethoxysilane. Monoliths were characterized by scanning electron microscopy, ²⁹Si nuclear magnetic resonance spectroscopy and N₂ adsorption–desorption. About 80% of the vinyl precursor was incorporated in the final materials, leading to 15.9 and 61.5% of Si atoms bonded to vinyl groups for 20% vinyltrimethoxysilane and 80% vinyltrimethoxysilane, respectively. The 80% vinyltrimethoxysilane monolith presents a lower surface area than 20% vinyltrimethoxysilane (159 versus 551 m²/g), which is nevertheless compensated by a higher vinyl surface density. Chromatographic properties were evaluated in reversed‐phase mode. Plots of ln(k) versus percentage of organic modifier were used to assess the reversed‐phase mechanism. Its high content of organic groups leads to high retention properties. Column efficiencies of 170 000 plates/m were measured for this 80% vinyltrimethoxysilane hybrid silica monolith. Long capillary monolithic columns (90 cm) were successfully synthesized (N = 120 000).