| 介孔二氧化硅-接枝胶原杂化材料的制备和表征(英) | |
| 引用本文： | 曹勇,周钰明,单云,鞠熀先,薛学佳. 介孔二氧化硅-接枝胶原杂化材料的制备和表征(英)[J]. 无机化学学报, 2005, 21(3): 331-336 |
| 作者姓名： | 曹勇 周钰明 单云 鞠熀先 薛学佳 |
| 作者单位： | 1. 南京大学化学系,生命分析化学教育部重点实验室,南京,210093;东南大学化学化工系,南京,210096 2. 东南大学化学化工系,南京,210096 3. 南京大学化学系,生命分析化学教育部重点实验室,南京,210093 |
| 基金项目： | 国家杰出青年科学基金(No.20325518)，国家自然科学基金(No.50377005，20275017)，江苏省社会发展基金(No.BK2003064)资助项目 |
| 摘 要： | 利用接枝胶原与介孔二氧化硅制备一种新型生物无机杂化材料。用甲基丙烯酸甲酯为接枝剂对胶原进行共聚改性制得接枝胶原。以正硅酸乙酯为模板，十二烷基三甲基溴化铵为表面活性剂，用一个简单的热处理过程制得介孔二氧化硅。介孔二氧化硅-接枝胶原杂化材料通过超声分散接枝胶原与介孔二氧化硅的混合物制得，其三维结构用X射线衍射表征，晶格参数a，b和c分别为0.68，0.37和1.64 nm，为正交晶型。氮气吸附-解吸等温线显示杂化材料的比表面积可达273 m2·g-1，孔体积为0.13 cm3·g-1，平均孔径3.4 nm，分布窄。该杂化材料在8～14 μm波长的红外发射率可低至0.323，在光电子学器件和红外隐身领域具有潜在应用价值。 |
| 关 键 词： | 杂化材料； 介孔材料； 胶原； 红外发射率 |
| 收稿时间： | 2004-10-08 |
| 修稿时间： | 2004-12-12 |
Preparation and Characterization of Grafted Collagen Confined in Mesoporous Silica |
|
| CAO Yong,ZHOU Yu-Ming,SHAN Yun,JU Huang-Xian and XUE Xue-Jia. Preparation and Characterization of Grafted Collagen Confined in Mesoporous Silica[J]. Chinese Journal of Inorganic Chemistry, 2005, 21(3): 331-336 | |
| Authors: | CAO Yong ZHOU Yu-Ming SHAN Yun JU Huang-Xian XUE Xue-Jia |
| Affiliation: | Department of Chemistry, Key Laboratory of Analytical Chemistry for Life Science, Department of Chemistry, Nanjing University, Nanjing 210093;Department of Chemistry and Chemical Engineering, Southeast University, Nanjing 210096,Department of Chemistry and Chemical Engineering, Southeast University, Nanjing 210096,Department of Chemistry and Chemical Engineering, Southeast University, Nanjing 210096,Department of Chemistry, Key Laboratory of Analytical Chemistry for Life Science, Department of Chemistry, Nanjing University, Nanjing 210093 and Department of Chemistry and Chemical Engineering, Southeast University, Nanjing 210096 |
| Abstract: | A novel hybrid biological-inorganic material was prepared by filling grafted collagen in mesoporous silica structure. The grafting was realized by reaction between collagen and methyl methacrylate monomer. The formation of mesoporous silica precursor using tetraethyl orthosilicate as a template and cetyltrimethylammonium bromide as an assembly surfactant was completed in ammonia system at room temperature. A simple calcination treatment produced the mesoporous silica structure. An ultrasonic dispersion process was employed to immobilize grafted collagen chain in a three-dimensional mesoporous silica structure. The XRD pattern showed the presence of a three-dimensional meso-structure with the a, b, and c parameters of 0.68, 0.37 and 1.64 nm. Nitrogen adtribution. The infrared emissivity of the composite at 8～14μm wavelength was 0.323, which was very low, indicating a potential application of the composite in areas such as photoelectronics and infrared camouflage. |
| Keywords: | hybrid mesopore material collagen infrared emissivity |