Synthesis of nanosized TiO2/SiO2 particles using microwave processes and their photocatalytic activity on the decomposition of orange II

The nanosized titania and TiO₂/SiO₂ particles were prepared by the microwave-hydrothermal method. The effect of physical properties TTIP/TEOS ratio and calcination temperature has been investigated. The major phase of the pure TiO₂ particle is of the anatase structure, and a rutile peak was observed above 800°C. In TiO₂/SiO₂ particles, however, no significant rutile phase was observed, although the calcination temperature was 900°C. No peaks for the silica crystal phase were observed at either silica/titania ratio. The crystallite size of TiO₂/SiO₂ particles decreases as compared to pure TiO₂ at high calcination temperatures. The TiO₂/SiO₂ particles show higher activity on the photocatalytic decomposition of orange II as compared to pure TiO₂ particles.