PEO-based composite lithium polymer electrolyte, PEO-BaTiO3-Li(C2F5SO2)2N

Polyethylene oxide (PEO) based polymer electrolytes with BaTiO₃ as filler and Li(C₂F₅SO₂)₂N as salt have been examined in lithium polymer batteries. The aluminum disolution potential in PEO-Li(C₂F₅SO₂)₂N was estimated to be 4.1 V vs. Li/Li⁺ at 80 °C, which was compared to that of 3.8 V vs. Li/Li⁺ in PEO-Li(CF₃SO₂)₂N. The electrical conductivity of the system was measured as a function of O/Li ratio. The highest conductivity was observed in O/Li=8. The conductivity was 1.65×10⁻³ S/cm at 80 °C and 1.5×10⁻⁵ S/cm at 25 °C. The interfacial resistance of Li/polymer electrolyte/Li annealed at 80 °C for 15 days was lower than 100 Ωcm². Paper presented at the 8th EuroConference on Ionics, Carvoeiro, Algarve, Portugal, Sept. 16 – 22, 2001.