Electrical resistivity and thermal conductivity of UP1−xSx

UP, US, and their solid solutions of several compositions were prepared, and the electrical resistivities of these samples were measured from liquid nitrogen temperature to 1000 K and the thermal diffusivities from 300 to 1000 K. It was shown that the resistivity of UP_1?xS_x at the paramagnetic region arose mainly from the scattering of conduction electrons by disordered spins localized at uranium ion sites. The resistivity of UP_0.4S_0.6 showed another anomaly below the transition temperature. A gentle hump of the thermal diffusivity of UP was observed at about 650 K. This was concluded to be due to the anomalous negative temperature coefficient of electrical resistivity observed above the Néel temperature up to about 550 K. The composition dependence of thermal conductivity of UP_1?xS_x was compared with that of UC_1?xN_x by separating the total conductivity into electronic and phonon contributions.