Preparation and magnetic properties of BaFe12O19/Ni0.8Zn0.2Fe2O4 nanocomposite ferrite

Nanocomposite of hard (BaFe₁₂O₁₉)/soft ferrite (Ni_0.8Zn_0.2Fe₂O₄) have been prepared by the sol–gel process. The nanocomposite ferrite are formed when the calcining temperature is above 800 °C. It is found that the magnetic properties strongly depend on the presintering treatment and calcining temperature. The “bee waist” type hysteresis loops for samples disappear when the presintering temperature is 400 °C and the calcination temperature reaches 1100 °C owing to the exchange-coupling interaction. The remanence of BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite with the mass ratio of 5:1 is higher than a single phase ferrite. The specific saturation magnetization, remanence magnetization and coercivity are 63 emu/g, 36 emu/g and 2750 G, respectively. The exchange-coupling interaction in the BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite is discussed.