| Nb对低碳Si-Mn钢连续冷却转变的影响 |
| |
| 引用本文： | 商艳,丁桦,李龙.Nb对低碳Si-Mn钢连续冷却转变的影响[J].东北大学学报(自然科学版),2008,29(2):221-224. |
| |
| 作者姓名： | 商艳 丁桦 李龙 |
| |
| 作者单位： | 1. 东北大学材料与冶金学院,辽宁沈阳,110004
2. 东北大学材料与冶金学院,辽宁沈阳,110004;东北大学轧制技术及连轧自动化国家重点实验室,辽宁沈阳,110004 |
| |
| 基金项目： | 国家自然科学基金，上海宝钢集团公司联合资助项目 |
| |
| 摘 要： | 利用Gleeble 1500对含Nb与不含Nb两种低碳Si-Mn钢进行了连续冷却转变实验,并绘制了未变形及变形条件下的CCT曲线.结果表明:在未变形条件下,Nb的添加降低了铁素体相变温度(Ar3),使未变形CCT曲线下移;在变形条件下,应变诱导析出的Nb(C,N)等析出物使铁素体的转变温度上升并降低了贝氏体的转变冷速,从而使Ar3提高,CCT曲线上移;在变形条件下,Nb使铁素体晶粒明显细化,进而使实验钢的硬度明显提高.
|
| 关 键 词： | Nb 连续冷却转变 固溶 应变诱导析出 |
| 文章编号： | 1005-3026（2008）02-0221-04 |
| 收稿时间： | 2007-04-23 |
| 修稿时间： | 2007年4月23日 |
Effect of Nb on Low-Carbon Si-Mn Steel During Continuous Cooling Transformation |
| |
| SHANG Yan,DING Hua,LI Long.Effect of Nb on Low-Carbon Si-Mn Steel During Continuous Cooling Transformation[J].Journal of Northeastern University(Natural Science),2008,29(2):221-224. |
| |
| Authors: | SHANG Yan DING Hua LI Long |
| |
| Institution: | (1) School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China; (2) State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, China |
| |
| Abstract: | The continuous cooling transformation(CCT) tests of low-carbon Si-Mn steel were conducted on Gleeble 1500 thermal simulator with and without Nb addition,and the relevant curves were plotted under deformed and undeformed conditions.The results showed that the undeformed CCT curves mostly go down due to the effect of Nb addition that lowers the phase transformation temperature of ferrite(Ar3),while the deformed CCT curves go up due to the effect of strain-induced precipitates as Nb(C,N),which raises Ar3 hence lowers the starting cooling rate in banite transformation.Moreover,ferrite grains were refined obviously with the addition of Nb under deformed conditions,thus hardening greatly the tested steel. |
| |
| Keywords: | Nb |