The effect of gamma irradiation on glass transition temperature and thermal stability of Se96Sn4 chalcogenide glass

Se₉₆Sn₄ chalcogenide glass was prepared by melt quenching technique and exposed, at room temperature, to different doses of 4, 8, 12, 24 and 33 kGy of high-energy ⁶⁰Co gamma irradiation. Differential scanning calorimeter (DSC) was used under non-isothermal condition to determine the glass transition temperature T_g, onset T_c and peak T_p temperatures of crystallization, of un-irradiated and γ-irradiated samples, at four different heating rates. The variation of T_g with heating rates was utilized to calculate the glass transition activation energy E_t for un-irradiated and γ-irradiated glass, using the methods suggested by Kissinger and Moynihan. Based on the obtained values of the characteristic temperatures T_g, T_c and T_p, thermal stability was monitored through the calculation of the S parameter and the crystallization rate factor 〈K_p〉 for irradiated and un-irradiated glass. Results reveal that, as γ-dose increases T_g increases up to 12 kGy then decreases at higher doses but remains more than that of un-irradiated glass. Meanwhile, both E_t and 〈K_p〉 attain their minimum values at the same dose of 12 kGy and the glass is thermally stable at this particular dose.