Styrene Butadiene Rubber/Epoxidized Natural Rubber (SBR/ENR50) Nanocomposites Containing Nanoclay and Carbon Black as Fillers for Application in Tire-Tread Compounds

Nanocomposite vulcunizates based on a SBR/ENR50 (50/50%wt) rubber blend containing nanoclay (5 or 10 phr) with and without carbon black (CB 20 phr) were prepared by melt blending in an internal mixer. The compound containing 35 phr carbon black (only) was prepared as a reference sample. Microstructure of nanocomposite samples was investigated by using X-ray diffraction (XRD), melt rheo-mechanical spectroscopy (RMS), and scanning electron microscopy (SEM). The XRD patterns revealed that the distance between the clay layers were increased by adding CB to the nanocomposite samples; they caused better diffusion of chains between the layers and resulted in an intercalated structure. The RMS results also indicated the formation of the filler-filler networks. SEM images of fracture surfaces showed the presence of much roughness in the samples containing both nanoclay and CB compared to the other samples. The results obtained from application of the Flory–Rhener equation showed a high crosslink density for the sample with 10 phr nanoclay and 20 phr CB. Dynamic mechanical behavior, mechanical properties, and abrasion resistance of the nanocomposites were evaluated. The results indicated that the sample containing 10 phr nanoclay and 20 phr CB had an increased dynamic elastic modulus, reduced maximum loss factor (tanδ)_max,, and an improved tensile strength and abrasion resistance compared to the reference sample. Also, this sample showed the lowest maximum loss factor, at 50–60°C, so it can be a candidate for tire-tread application.