The Effect of Talc on the Mechanical,Crystallization and Foaming Properties of Poly(Lactic Acid)

Poly(lactic acid) (PLA)/talc composites containing different contents of talc were prepared by melt blending. Multiple properties of the prepared composites were investigated including mechanical, rheological and crystallization as well as foaming properties. Tensile test results indicated that the mechanical properties of the composite with 3% wt. talc showed significant reinforcement and toughening effect. When the talc content reached 10%, Young's modulus of the composite was increased by 35% compared with pure PLA. The morphological results showed that the talc layers were partially delaminated and uniformly dispersed in the PLA matrix at low loading. Differential scanning calorimetry (DSC) and polarized optical microscopy (POM) results indicated that 3% wt. talc significantly increased the crystallinity of the PLA matrix. The thermogravimetric analysis (TGA) results demonstrated that the thermal stability of PLA/talc composites was enhanced as well. Moreover, talc at low loading could act as a plasticizer in the polymer flow, which was investigated by rheological tests. The batch foaming experiments revealed that 3% wt. talc loading had the most notable heterogeneous nucleation effect, with the cell size decreasing from 15.4 μm for neat PLA to 8.5 μm and the cell density increasing by 298%.