Preparation,characterization and thermal decomposition of phenylenediammonium sulfate salts Part. XVI

Polyaniline/α-Al₂O₃ (PANI/α-Al₂O₃) composites were synthesized by in situ polymerization through ammonium persulfate ((NH₄)₂S₂O₈, APS) oxidized aniline using HCl as dopant. XRD and FTIR were used to characterize the PANI/α-Al₂O₃ composites. The thermal stabilities and glass transition temperature (T _g) of PANI/α-Al₂O₃ composites were tested using thermogravimetric (TG) method and modulated differential scanning calorimetry (MDSC) technique. The results of TG showed that the thermal stability of PANI/α-Al₂O₃ composite increased and then decreased with the increase in α-Al₂O₃ content. The derivative thermogravimetry (DTG) curves showed one step degradation of PANI when the α-Al₂O₃ content was lower than 52.5 mass%, and exhibited two steps degradation when the α-Al₂O₃ content was higher than 63.6 mass%. The MDSC curves showed that the T _g of PANI/α-Al₂O₃ composites increased and then decreased with the augment of α-Al₂O₃ for the interaction between PANI chains and the surface of α-Al₂O₃.