Curing characteristics of carboxyl functionalized glucose resin and epoxy resin

The curing characteristics of carboxylic functionalized glucose resin (glucose maleic acid ester vinyl resin: GMAEV) and epoxy resin have been studied using DSC and FTIR methods. Exothermic reactions attributed to esterification and etherification reactions of the hydroxyl and carboxyl functionalities of GMAEV with the epoxy groups were identified. Exothermic reactions showed very different patterns according to the degree of carboxyl group substituent of GMAEV. The results showed that esterification reaction occurs in the early stage of cure and then etherification followed after completion of the esterification. A cured matrix containing epoxy resin and 50 wt.% of GMAEV was prepared and characterized. The cured matrix showed thermal stability up to 300 °C. The average glass transition temperature and storage modulus of the matrix were as high as 95 °C and 2700 MPa, respectively. The cured matrix of epoxy resin and GMAEV with higher degree of carboxyl group was found to have a lower density due to the formation of bulky groups in the crosslinks.