Synthesis of nanosized TiO2 powder by sol gel method at low temperature |
| |
Authors: | W. Nachit S. Touhtouh Z. Ramzi M. Zbair A. Eddiai M. Rguiti |
| |
Affiliation: | 1. Laboratory of Coordination and Analytical Chemistry (LCCA (E2M)), Department of Chemistry, Faculty of Sciences, Chouaib Doukkali University, El Jadida, Morocco;2. Engineering Sciences Laboratory For Energy(LabSIPE), National School of Applied Sciences(ENSA), Chouaib Doukkali University, Plateau, El Jadida, Morocconachit.wafaa@gmail.com;4. Engineering Sciences Laboratory For Energy(LabSIPE), National School of Applied Sciences(ENSA), Chouaib Doukkali University, Plateau, El Jadida, Morocco;5. Engineering Sciences Laboratory For Energy(LabSIPE), National School of Applied Sciences(ENSA), Chouaib Doukkali University, Plateau, El Jadida, Morocco;6. Laboratory of Catalysis and Corrosion of Materials (LCCM), Department of Chemistry, Faculty of Sciences, Chouaib Doukkali University, El Jadida, Morocco;7. Laboratory of Condensed Matter Physics, Faculty of Sciences Ben M'sik, Hassan II University, Casablanca, Morocco;8. Laboratory of Ceramic Materials and Processes (LMCPA), Maubeuge University, Maubeuge, France |
| |
Abstract: | ABSTRACTNanotechnology is all about making products from very small constituents, components or subsystems to gain greatly enhanced material properties and functionality. Nanocrystalline anatase TiO2 was prepared by a facile sol–gel route at a temperature of 50°C under mild conditions. Titanium tetraisopropoxide (TTIP) was used as a titanium precursor, and 2-propanol was used as a solvent. XRD, TEM, SEM, FT-IR and BET were applied to characterize the crystal phase. The Crystalline size of TiO2 powder has been obtained with diameter < 30 nm for anatase at 500°C using an acid. |
| |
Keywords: | Titanium dioxide sol-gel nanocristallites Anatase |
|
|